Karakterisasi Nanoselulosa dari Tandan Kosong Aren (Arenga pinnata) sebagai Filler dalam Pembuatan Tisu
Characterization of Nanocellulose from Empty Bunches of Aren (Arenga pinnata) as Filler in Tissue Manufacturing
DOI:
https://doi.org/10.25026/jsk.v6i1.2156Abstract
The high demand for tissue made from wood as the main raw material has led to the shrinkage of Indonesian forests. Nanocellulose from empty palm bunches was prepared in this study by delignification, hydrolysis and ultrasonication in order to obtain the optimum ultrasonification time. Time variations were 15 min, 30 min and 45 min at 50°C. FTIR analysis showed wavelengths for ?-cellulose functional groups of empty palm bunches, namely O-H groups at 3042.43 cm-1, C-H at 2900.94 cm-1 and C-O at 1049.28cm-1. FE-SEM analysis showed that nanocellulose with 45 min ultrasonification time has a particle size that meets the criteria of nanoparticles. The addition of nanocellulose in napkins increased the thickness and water absorption, with the addition of 6 g of nanocellulose giving the most significant results. With further research, the utilization of TKA in the tissue industry can help to reduce pressure on forests and provide a sustainable alternative for tissue production.
Keywords: Nanocellulose, Aren Empty Bunch, Filler
Abstrak
Tingginya permintaan tisu yang terbuat dari kayu sebagai bahan baku utamanya telah menyebabkan penyusutan hutan Indonesia. Nanoselulosa tandan kosong aren dibuat dalam penelitian ini melalui proses delignifikasi, hidrolisis dan ultrasonifiasi dengan tujuan untu mendapatkan waktu ultrasonifikasi yang optimum. Metode penelitian yang digunakan meliputi proses delignifikasi, hidrolisis asam serta ultrasonifikasi. Variasi waktu yang dilakukan 15 menit, 30 menit dan 45 menit pada suhu 50oC. Hasil analisis FTIR menunjukkan panjang gelombang untuk gugus fungsi ?-selulosa tandan kosong aren yaitu gugus O-H pada daerah 3042,43 cm-1, C-H pada 2900,94 cm-1 dan C-O 1049,28cm-1 . Hasil analisis FE-SEM menunjukkan bahwa nanoselulosa dengan lama waktu ultrasonifikasi 45 menit memiliki ukuran partikel yang memenuhi kriteria nanopartikel. Penambahan nanoselulosa dalam tisu napkins meningkatkan ketebalan dan daya serap air, dengan penambahan 6 gr nanoselulosa memberikan hasil yang paling signifikan. Dengan penelitian lebih lanjut, pemanfaatan TKA dalam industri tisu dapat membantu mengurangi tekanan terhadap hutan dan menyediakan alternatif yang berkelanjutan untuk produksi tisu.
Kata Kunci: Nanoselulosa, Tandan Kosong Aren, Filler
References
Grieser, F., Ashokkumar, M., and Sostric, J. Z. 1999. Sonochemistry and Sonoluminescence. (Netherlands: Kluwer Academic Publishers.
Yanti, H. and Tang, M. (2021) ‘Pemanfaatan Limbah Padat Tahu Sebagai Bahan Baku Pembuatan Tisu dengan Metode Acetosolv’, SAINTIS, 2(1): 28-33.
Sijabat, E. K., Sakti, S. A., & Prijadi, B. T. (2022). Aplikasi Nanocrystalline Cellulose dari Proses Hidrolisis Asam sebagai Reinforced Material pada Kertas Facial Tissue. Fluida, 15(2), 73-81.
Wirawan, S.K. et al. (2015) ‘Peningkatan Mutu Serat Daur Ulang Kotak Karton Gelombang Bekas Menggunakan CMC’, Jurnal Selulosa, 5(1): 33-57.
Hidayatullah, I. et al. (2022). ‘Kajian Pustaka Sintesis Nanoselulosa Dari Tandan Kosong Kelapa Sawit Sebagai Filler Pembuatan Tisu Toilet’, Jurnal Fluida, 15(1): 51-59.
Silitonga, N., Tarigan, N., & Saragih, G. (2019). Pengaruh kosentrasi naoh pada karakterisasi ?-selulosa dari pelepah kelapa sawit. Ready Star, 2(1), 103-108.
Wirjosentono, B. (2014). Preparation and characterization of nanocrystalline cellulose from sugar palm bunch (Arenga pinnata (Wurmb) Merr.). International Journal of PharmTech Research, 6(2), 814-820.
Fatsan, A. et al. (2020) ‘Potensi Hasil dan Keragaman Fenotipik Aren (Arenga Pinnata (Wurmb) Merr.) Sulawesi Tenggara Potential Yield and Diversity of Phenotypic of Palm Sugar (Arenga Pinnata (Wurmb) Merr.) in Southeast Sulawesi’, J. Berkala Penelitian Agronomi, 8(2): 7-15.
Apriyani, I. dan Rahmawati, F. (2021) ‘Pembuatan Elektroda Karbon Aktif dari Tandan Kosong Buah Aren Dengan Variasi Suhu Karbonisasi’, Komunikasi Fisika Indonesia, 18(1): 58-63.
Maria, E. W. et al. (2019) ‘Production Nanocellulose from Raw Materials for Oil Palm Empty Bunches (Tkks) with Hydrolysis and Freeze Drying Methods’, In Iop Conference Series: Materials Science and Engineering. Institute of Physics Publishing. 1(2): 1-8.
Viana, L.C. et al. (2018) ‘Nanofibrillated Cellulose as an Additive for Recycled Paper’, Cerne, 24(2): 140–148.
Fessenden, Kimia Organik. Edisi ketiga. (Jakarta: Erlangga, 1986).
Farma, R. et al. (2022) ‘Hemicellulosa-Derived Arenga Pinnata Bunches as Free Standing Carbon Nanofiber Membranes for Electrode Material Supercapacitors’, Scientific Reports, 12(1): 1-11.
Chen, L., Wang, Q., Hirth, K., Baez, C., Agarwal, U. P., & Zhu, J. Y. (2015). Tailoring the yield and characteristics of wood cellulose nanocrystals (CNC) using concentrated acid hydrolysis. Cellulose, 22(3), 1753–1762.
Fatah, I. Y. A., Abdul Khalil, H. P. S., Hossain, M. S., Aziz, A. A., Davoudpour, Y., Dungani, R., & Bhat, A. (2014). Exploration of a chemomechanical technique for the isolation of nanofibrillated cellulosic fiber from oil palm empty fruit bunch as a reinforcing agent in composites materials. Polymers, 6(10), 2611–2624.
Hu, Z., Zhai, R., Li, J., Zhang, Y., & Lin, J. (2017). Preparation and characterization of nanofibrillated cellulose from bamboo fiber via ultrasonication assisted by repulsive effect. International Journal of Polymer Science, 2017.
Hendrawati, N., Dewi, E. N., & Santosa, S. (2019). Karakterisasi Biodegradable Foam dari Pati Sagu Termodifikasi dengan Kitosan Sebagai Aditif. Jurnal Teknik Kimia Dan Lingkungan, 3(1), 47
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2024 Jurnal Sains dan Kesehatan
This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.